Description
Two component Epoxy based anti corrosive primer pigmented with Zinc Chromate as corrosion inhibiting pigments.
It is recommended as primer on M.S surface for original equipment manufacturing as well as for process industry as in various fertilizer, refineries, petrochemical, chemical and other plants, applied in diverse areas of tank exteriors, equipments, pipelines, structural steel, etc. Not to be used for immersion application.
| COLOUR | : Assorted |
|---|---|
| FINISH | : Matt |
| SOLIDS BY VOLUME | : 40 ± 3% |
| THEORETICAL SPREADING RATE | : 13.33 sq.mt. / ltr. at recommended DFT of 30 µ |
| FLASH POINT | : Base : Above 23°C Hardener : Above 23°C |
| DRYING CHARACTERISTICS | : SURFACE DRY : 60 90 minutes |
| (At 65% Relative Humidity & at 30°C) | : HARD DRY : Overnight FULL CURE : 7 days |
| SHELF LIFE | : BASE : 6 months HARDENER : 6 months |
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be cleaned to St-2/St-3 std. The surface should be absolutely dry, moisture and oil free before primer application.
| MIXING RATIO | : Base : Hardener (As per our recommendations) |
|---|---|
| APPLICATION | : By Brush / By Conventional Spray |
| THINNER | : Epoxy thinner 190 |
| POT LIFE | : 4 hours min at 30°C |
| RECOMMENDED DFT | : 30 - 40 µ. |
| OVERCOATING INTERVAL | : MIN : 8 hours MAX : 24 hours |
| COMPATIBILITY | : Can be over coated with Epoxy, PU, Chlorinated rubber and Oleo-resinous topcoats. |
Stir the Base part thoroughly. Mix the base and hardener as per our recommended ratio, by volume. Stir the mix gently to attain homogeneity. Allow the mixture to stand still (maturation) for about 10-15 minutes to initiate the reaction. Add Epoxy Thinner into the mix, if required, depending on application method, and stir gently for few minutes. Strain the paint through Nylon filter cloth of 100 mesh size and apply uniformly over the surface. All equipments used for above should be properly cleaned.
Application :- By Brush / By Conventional Spray / By Airless Spray
Generally no thinner is required for Brush application, however under adverse environmental conditions about 5% of thinner, by volume, can be added. Apply evenly in criss-cross manner and ensure the uniform application. Use quality brushes for paint application
| Thinner : | Epoxy Thinner 190 |
|---|---|
| Addition : | 10-15% |
| Nozzle Orifice : | 1.2 -1.4 mm |
| Nozzle Pressure : | 40-70 psi |
| Thinner : | Epoxy Thinner 190 |
|---|---|
| Addition : | 10-15% |
| Addition : | Max 5% if required |
| Nozzle Orifice : | 0.37- 0.42mm |
| Nozzle Pressure : | 1400-1800 psi |
1. Do not apply paint when temperature falls below 10°C or rises above 50°C and when Relative Humidity is above 85% or during rain, fog or mist. Surface temperature must always be minimum of 3°C above Dew point.
2. Brushes and spray equipment should be cleaned with SAFFRO's recommended thinner otherwise equipment is liable to be damaged.
3. DFT variation can be obtained by change in application method/thinning ratio.
4. Shelf life indicated is minimum for this Product in sealed conditions and it is subject to re-inspection thereafter. Individual component is required to be stored in cool, dry and covered condition, away from heat and ignition
This is a solvent based paint and care should be taken to avoid inhalation of spray mist or vapours as well as contact between the wet paint and exposed skin or eyes.
To the best of our knowledge, the technical data in our literature are true and accurate at the date of issuance but are subject to change without prior notice. We guarantee our product to conform to the specifications contained herein. We make no other warranty or guarantee of any kind, express or implied, including merchantability and fitness for particular purpose. Liability, if any, is limited to replacement of the product or refund of the purchased price. Labour or cost of labour and other consequential damages are hereby excluded.